Sikaflex®-221 Multi-purpose adhesive sealant with a wide adhesion range

Short Description:

Sikaflex®-221 is a multi-purpose 1-component polyurethane adhesive / sealant that bonds well to a wide variety of substrates like metals, metal primers and paint coatings (2-component systems), ceramic materials and plastics. It is suitable for making permanent elastic seals.  


  • Packaging: Cartridge 300 ml Unipack 400ml/600 ml
  • Product Detail

    Product Tags

    Features &Benefits

    • -Bonds well to a wide variety of substrates
    •  
    • -Resistant to ageing
    •  
    • -Can be sanded and painted
    •  
    • -Passes EN45545-2 R1/R7 HL3
    •  
    • -Non-corrosive
    •  
    • -Low odor

    Typical Product Data

    Chemical base   1-component polyurethane

     

    Color (CQP001-1)   White, steel grey, black

     

     

    Cure mechanism   Moisture-curing
    Density (uncured) depending on color 1.3 kg/l
    Non-sag properties   Good
    Application temperature ambient 5 ─ 40 °C

     

    Skin time (CQP019-1)   60 minutes A
    Open time (CQP526-1)   45 minutes A

     

     

    Curing speed (CQP049-1)   (see diagram)
    Shrinkage (CQP014-1)   5 %
    Shore A hardness (CQP023-1 / ISO 7619-1)   40
    Tensile strength (CQP036-1 / ISO 527)   1.8 MPa
    Elongation at break (CQP036-1 / ISO 527)   500 %
    Tear propagation resistance (CQP045-1 / ISO 34)   7 N/mm
    Service temperature (CQP513-1)  

    24 hours

    1 hour

     

    -50 ─ 90 °C

    120 °C

    140 °C

     

    Shelf life (CQP016-1)   12 months B

     

    CQP = Corporate Quality Procedure A) 23 °C / 50 % r.h. B) storage below 25 °C

     

    Cure Time

     

    CURE MECHANISM

    Sikaflex®-221 cures by reaction with atmospheric moisture. At low temperatures the water content of the air is generally lower and the curing reaction proceeds somewhat slower (see diagram 1).

    221

    Diagram 1: Curing speed for Sikaflex®-221

    CHEMICAL RESISTANCE

    Sikaflex®-221 is generally resistant to fresh water, seawater, diluted acids and diluted caustic solutions; temporarily resistant to fuels, mineral oils, vegetable and animal fats and oils; not resistant to organic acids, glycolic alcohol, concentrated mineral acids and caustic solutions or solvents.

    Applications

    Surface preparation

    Surfaces must be clean, dry and free from grease, oil and dust.

    Surface treatment depends on the specific nature of the substrates and is crucial for a long lasting bond. Suggestions for surface preparation may be found on the current edition of the appropriate Sika® Pre-Treatment Chart. Consider that these suggestions are based on experience and have in any case to be verified by tests on original substrates.

    Application

    Sikaflex®-221 can be processed between 5 °C and 40 °C but changes in reactivity and application properties have to be considered. The optimum temperature for substrate and sealant is between 15 °C and 25 °C.

    Sikaflex®-221 can be processed with hand, pneumatic or electric driven piston guns as well as pump equipment. For advice on selecting and setting up a suitable pump system, contact the System Engineering Department of Sika Industry.

     

    Tooling and finishing

    Tooling and finishing must be carried out within the skin time of the sealant. It is recommended using Sika® Tooling Agent N. Other finishing agents must be tested for suitability and compatibility prior the use.

    Removal

    Uncured Sikaflex®-221 can be removed from tools and equipment with Sika® Remover-208 or another suitable solvent. Once cured, the material can only be removed mechanically. Hands and exposed skin have to be washed immediately using hand wipes such as Sika® Cleaner-350H or a suitable industrial hand cleaner and water. Do not use solvents on skin.

    Overpainting

    Sikaflex®-221 can be painted after formation of a skin. If the paint requires a baking process, best performance is achieved by allowing the sealant to fully cure first. 1C-PUR and 2C-acrylic based paints are usually suitable. All paints have to be tested by carrying preliminary trials under manufacturing conditions. The elasticity of paints is usually lower than of sealants what could lead to cracking of the paint film in the joint area.

    Usage

    Sikaflex®-221 bonds well to a wide variety of substrates and is suitable for making permanent elastic seals . Suitable substrate materials are metals, metal primers and paint coatings (2-component systems), ceramic materials and plastics. It is ideally used for internal sealing and simple bonding applications. Seek manufacturer’s advice and perform tests on original substrates before using Sikaflex®-221 on materials prone to stress cracking. This product is suitable for experienced professional users only. Test with actual substrates and conditions have to be performed to ensure adhesion and material compatibility.  