WACKER® CS – CONSTRUCTION SEAL SEILICONE SEALANT
Features &Benefits
- -excellent weatherability
- -excellent tooling characteristics for professional use
- -non-corrosive to metals
- -suitable for alkaline substrates such as concrete, mortar, fibrous cement
- -matt finish
- -excellent adhesion on most substrates without primer
- -solvent-free, thus featuring low volume shrinkage during vulcanization
- -ready gunnability at low (+ 5 °C) and high (+ 40 °C) temperatures
- -flexible at low (-40 °C) and high temperatures (+150 °C)
- -almost odorless
- -non-sag
Applications
-Exterior Applications
-Silicone Sealants WACKER Brand
Application fields
- sealing of connection and expansion joints in the building industry
- sealing of perimeter joints
- sealing of joints between glazing and supporting structures (frames, transoms, mullions)
Processing
The substrate areas that will be in contact with the sealant must be clean, dry and free of all loose material, dust, dirt, rust, oil and other contaminants. Non-porous substrates should be cleaned with a solvent and a clean, lint-free, cotton cloth. Remove residual solvent before it evaporates with a fresh clean, dry cloth.
For application from cartridges cut thread open, fix nozzle on top and cut to required bead size. The sealant can be applied in beads or layers. It requires moisture in order to cure. The curing time can take longer at lower temperatures, lower humidity or by low volume of air exchange.
The use of tooling agents should be avoided if possible. Otherwise, water or a diluted solution of a little neutral soap or alcohol in water should be sparingly applied.
Certification
WACKER® CS - CONSTRUCTION SEAL is certified and classified according to
- ISO 11600 F/G, Class 20 LM
- EN 15651-1, Class 20LM F-EXT-INT-CC
- EN 15651-2, Class 20LM G-CC
- ASTM C920, Class 35
Adhesion
WACKER® CS - CONSTRUCTION SEAL exhibits excellent primerless adhesion to many substrates, e.g. glass, tiles, ceramics, enamel, glazed tiles and clinker e.g. aluminium, steel, zinc or copper wood, and many plastics. Users must carry out their own tests due to the great variety of substances. The adhesion can be improved in many cases by pretreatment of the substrates with a primer. If adhesion difficulties arise please contact our technical service.
Restrictions on use
It is the user's responsibility to test the compatibility of the sealant with the adjoining materials. Incompatible substances like coating materials (paints, varnishes and glazes) or organic plasticizer containing rubbers (EPDM, butyl and neoprene) can lead to discoloration or other impairments like loss of adhesion of the sealant. Materials in direct contact with the applied sealant like cleaning agents and materials in indirect contact like gaseous emissions can damage the sealant in its function or change its appearance. Because of the multitude of these materials Wacker cannot make a general statement to the compatibility of materials with the sealant. In case of doubt the user shall conduct appropriate preliminary tests. The time until complete curing may be extended at lower temperature, lower humidity, increasing film thickness or by low volume of air exchange. Otherwise, water or a diluted solution of a little neutral soap or alcohol in water should be sparingly applied.
WACKER® CS - CONSTRUCTION SEAL must not be used for insulating glass applications.
WACKER® CS - CONSTRUCTION SEAL is not recommended for structural glazing bonding.
WACKER® CS - CONSTRUCTION SEAL may be discolored in contact with some organic elastomers, e.g. EPDM, APTK and neoprene.
WACKER® CS - CONSTRUCTION SEAL is not recommended for use on natural stones, such as marble, granite, quartzite, as it can cause staining. In this case use an alternative grade such as WACKER® 460 - NATURAL STONE.
WACKER® CS - CONSTRUCTION SEAL is not recommended for sealing of aquaria or for long term use under water
WACKER® CS - CONSTRUCTION SEAL is not suitable for food grade applications where the joints are likely to come in contact with food. For this application WACKER® 120 - FOOD AND WATER has been developed
WACKER® CS - CONSTRUCTION SEAL is not suitable for use as a mirror adhesive.
How to Use
Properties Uncured
Property
|
Condition
|
Value
|
Method
|
---|---|---|---|
Skin forming time | 23 °C | 50 % r.h | 15 - 25 min | - |
Density | 23 °C | 1.40 g/cm³ | ISO 1183-1 A |
Consistency | - | non-sag | ISO 7390, profile U 20 |
Extrusion rate - mass flow | 6 bar | 23 °C | 130 g/min | - |
These figures are only intended as a guide and should not be used in preparing specifications.
Properties Cured
Property
|
Condition
|
Value
|
Method
|
---|---|---|---|
Movement capability | - | 20 % | ISO 11600 |
Movement capability | - | 35 % | ASTM C920 |
Modulus at 100 % elongation | - | 0.40 N/mm² | ISO 8339 |
Modulus at 100 % elongation | - | 0.38 N/mm² | ISO 37 |
Elongation at break | - | 250 % | ISO 8339 |
Elongation at break | - | 560 % | ISO 37 |
Hardness Shore A | - | 22 | ISO 868 |
Tensile strength | - | 0.50 N/mm² | ISO 8339 |
Tensile strength | - | 0.38 N/mm² | ISO 37 |
These figures are only intended as a guide and should not be used in preparing specifications.